Abstract
A new route of emulsifier-free emulsion polymerization based on the homogenous mechanism was investigated to prepare magnetic nanoparticles coated by poly (methyl methacrylate) (PMMA). The experimental results confirm the formation of PMMA thin and unique layers covering magnetite cores. The polymer layer thickness, determined from transmission electron microscopy (TEM) images, increases from 4.3 nm to 6.8 nm with increasing mass ratio of MMA to magnetite from 3:1 to 11:1. The increase of the polymer thickness results in the decrease in magnetization saturation of polymeric coated magnetic particles. However, this reduction, no more than 13 emu g−1, is much lower compared to that in other studies with the presence of surfactants or emulsifiers. Besides, the dispersion stability of the prepared particles is significantly improved.