Enhanced catalytic activity of zeolitic imidazolate frameworks (ZIF-8) polyelectrolyte complex composites membranes by laser etching Cover

Enhanced catalytic activity of zeolitic imidazolate frameworks (ZIF-8) polyelectrolyte complex composites membranes by laser etching

Materials Science-Poland
Volume 42 (2024): Issue 1 (March 2024)
By: Ting Yu,  Boonyarach Kitiyanan and  Stephan Thierry Dubas  
Open Access
|May 2024

Figures & Tables

Fig. 1.

(a) XRD patterns of ZIF-8 and calcined ZIF-8, (b) FE-SEM images of calcined ZIF-8

Fig. 2.

Pictures of PECs that (a) 0ZIF/PEC, (b) 10ZIF/PEC, (c) 30ZIF/PEC, (d) 50ZIF/PEC, (e) 70ZIF/PEC and (f) 90ZIF/PEC

Fig. 3.

Photo of PECs before (left side) and after (right side) laser etching

Fig. 4.

FE-SEM images of (a) 0ZIF/PEC-L, (b) 10ZIF/PEC-L, (c) 30ZIF/PEC-L, (d) 50ZIF/PEC-L, (e) 70ZIF/PEC-L, and (f) 90ZIF/PEC-L

Fig. 5.

FE-SEM images of xZIF/PEC etched by laser (left side) and corresponding EDS mapping of Zn distribution (right side): (a) 10ZIF/PEC-L, (b) 30ZIF/PEC-L, (c) 50ZIF/PEC-L, (d) 70ZIF/PEC-L and (e) 90ZIF/PEC-L

Fig. 6.

XRD patterns of 70ZIF/PEC before and after laser etching

Fig. 7.

ATR-FTIR spectra of PDDA, PSS, ZIF-8, 70ZIF/PEC, and 70ZIF/PEC-L

Fig. 8.

Triglyceride conversion catalyzed by ZIF/PECL with 10%, 30%, 50%, 70%, and 90% ZIF-8 loadings over five times usages

Fig. 9.

Conversion of triglyceride in soybean oil by powder calcined ZIF-8, PDDA/PSS PEC, 70ZIF/PEC, 70ZIF/PEC-L, and blank experiment

Fig. S1.

(a) The schematic of batch reactor for transesterification, and (b) Photograph of batch reactor for transesterification

Fig. S2.

HPLC chromatograms of (a) soybean oil, FAME converted from soybean oil by (b) no catalyst under 150°C for 4 hours, (c) PDAD/PSS PECs under 150°C for 4 hours, (d) calcined ZIF-8 under 150°C for 4 hours, (e) ZIF-8-L under 150°C for 4 hours, (f) 70ZIF/PEC under 150°C for 4 hours, (g) 70ZIF/PEC-L under 150°C for 4 hours. The conditions of HPLC: an Inertsil ODS-4 column (250 mm × 4.6 mm × 5 μm) and a mixture mobile phase consisting of acetone/acetonitrile (80:20 V/V) was used at an oven temperature of 30°C, a flow rate of 0.3 mL/min and a UV wavelength of 205 nm [1].

Fig. S3.

GC chromatograms of (a) Supelco 37 component FAME mix (C4:0, C6:0, C8:0, C10:0, C11:0, C12:0, C13:0, C14:0, C15:0, C17:0, C18:0, C20:0, C21:0, C22:0, C23:0, C24:0 C14:1, C15:1, C16:1, C17:1, trans-C18:1, cis-C18:1, C20:1, C22:1, C24:1, trans-C18:2, cis-C18:2, C18:3n6, C18:3n3, C20:2, C20:3n6, C2:4n6, C20:3n3, C20:5n3, C22:2n6, C22:6), FAME converted from soybean oil by (b) 10ZIF/PEC-L under 150°C for 4 hours, 1st usage (c) 30ZIF/PEC-L under 150°C for 4 hours, 1st usage (d) 50ZIF/PEC-L under 150°C for 4 hours, 1st usage (e) 70ZIF/PEC-L under 150°C for 4 hours, 1st usage, (e) 90ZIF/PEC-L under 150°C for 4 hours, 1st usage

Fig. S4.

FE-SEM image of 70ZIF/PEC after laser etching

Fig. S5.

Conversion of triglyceride in soybean oil by ZIF-8 and ZIF-8 exposed to laser
DOI: https://doi.org/10.2478/msp-2024-0004 | Journal eISSN: 2083-134X | Journal ISSN: 2083-1331
Journal RSS Feed
Language: English
Page range: 52 - 61
Submitted on: Jan 5, 2024
|
Accepted on: Mar 28, 2024
|
Published on: May 8, 2024
Published by: Wroclaw University of Science and Technology
In partnership with: Paradigm Publishing Services
Publication frequency: 4 issues per year
Keywords:
PECs,
ZIF-8,
laser,
etching
Related subjects:
Materials sciences,
Materials sciences, other,
Nanomaterials,
Functional and smart materials,
Materials characterization and properties

© 2024 Ting Yu, Boonyarach Kitiyanan, Stephan Thierry Dubas, published by Wroclaw University of Science and Technology
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Previous articleVolume 42 (2024): Issue 1 (March 2024)Next article