Effects of Al doping on defect behaviors of ZnO thin film as a photocatalyst
By: Fucheng Yu, Hailong Hu, Bolong Wang, Haishan Li, Tianyun Song, Boyu Xu, Ling He, Shu Wang and Hongyan Duan
Authors
Fucheng Yu
School of Material Science and Engineering, School of Mechanical and Electrical Engineering, Lanzhou University of Technology, Lanzhou, China
Hailong Hu
School of Material Science and Engineering, School of Mechanical and Electrical Engineering, Lanzhou University of Technology, Lanzhou, China
Bolong Wang
School of Material Science and Engineering, School of Mechanical and Electrical Engineering, Lanzhou University of Technology, Lanzhou, China
Haishan Li
School of Material Science and Engineering, School of Mechanical and Electrical Engineering, Lanzhou University of Technology, Lanzhou, China
Tianyun Song
School of Material Science and Engineering, School of Mechanical and Electrical Engineering, Lanzhou University of Technology, Lanzhou, China
Boyu Xu
School of Material Science and Engineering, School of Mechanical and Electrical Engineering, Lanzhou University of Technology, Lanzhou, China
Ling He
School of Material Science and Engineering, School of Mechanical and Electrical Engineering, Lanzhou University of Technology, Lanzhou, China
Shu Wang
School of Material Science and Engineering, School of Mechanical and Electrical Engineering, Lanzhou University of Technology, Lanzhou, China
Hongyan Duan
School of Material Science and Engineering, School of Mechanical and Electrical Engineering, Lanzhou University of Technology, Lanzhou, China
Language: English
Page range: 437 - 445
Submitted on: Jul 7, 2018
Accepted on: Apr 23, 2019
Published on: Oct 18, 2019
Published by: Wroclaw University of Science and Technology
In partnership with: Paradigm Publishing Services
Publication frequency: 4 issues per year
Keywords:
Related subjects:
© 2019 Fucheng Yu, Hailong Hu, Bolong Wang, Haishan Li, Tianyun Song, Boyu Xu, Ling He, Shu Wang, Hongyan Duan, published by Wroclaw University of Science and Technology
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.