Preparation of nanosized NaA zeolite and its surface modification by KH-550

Jin Hou; Qiwang Jiang

doi:10.2478/msp-2018-0083

Abstract

Nanosized NaA zeolite was successfully synthesized by hydrothermal method using tetraethyl orthosilicate (TEOS) and aluminum isopropoxide (AIP) as the main raw materials. The surface modification of NaA zeolite was carried out by silane coupling agent 3-aminopropyltriethoxysilane (KH-550). The effects of silane coupling agent dosage, reaction temperature, reaction time, hydrolysis time and pH value on grafting rate of NaA zeolite were investigated in detail. The zeolites were characterized by XRD, SEM-EDS, FT-IR and TG-DTA. The results showed that the surface of NaA zeolite was modified successfully by KH-550. The optimal modification conditions obtained were as follows: the dosage of coupling agent in 95 % ethanol – 1.6 %, reaction temperature − 70 °C, reaction time – 2 h, hydrolysis time – 20 min, and pH value – 3.5. Under these conditions, the grafting rate of modified NaA zeolite was 3.95 %.

References

[1] Hou J., Yuan J.S., Xu J., Fu Y.P., Meng C.X., Particuology, 11 (2013), 786.10.1016/j.partic.2012.12.001
Open DOI Search in Google Scholar Back to article
[2] Saceda J.F., Rintramee K., Khabuanchalad S., Prayoonpokarach S., LeonR. L., Wittayakun J., J. Ind. Eng. Chem., 18 (2012), 420.10.1016/j.jiec.2011.11.108
Open DOI Search in Google Scholar Back to article
[3] Yousef R.I., El-Eswed B., Al-Muhtaseb A.H., Chem. Eng. J., 171 (2011), 1143.10.1016/j.cej.2011.05.012
Search in Google Scholar Back to article
[4] Ikeda T., Nagase T., Hiyoshi N., Oumi Y., Micropor. Mesopor. Mat., 163 (2012), 42.10.1016/j.micromeso.2012.06.008
Search in Google Scholar Back to article
[5] Meng T., Ren N., Ma Z., J. Mol. Catal. A-Chem., 404 – 405 (2015), 233.10.1016/j.molcata.2015.05.006
Search in Google Scholar Back to article
[6] Fu Y.J., Hu C.C., Lee K.R., Lai J.Y., Desalination, 193 (2006), 119.10.1016/j.desal.2005.07.049
Search in Google Scholar Back to article
[7] Berry M.B., Libby B.E., Rose K., Haas K.H., Thompson R.W., Micropor. Mesopor. Mat., 39 (2000), 205.10.1016/S1387-1811(00)00198-0
Search in Google Scholar Back to article
[8] Yong H.H., Park H.C., Kanga Y.S., J. Membrane Sci., 188 (2001), 151.10.1016/S0376-7388(00)00659-1
Search in Google Scholar Back to article
[9] Suer M.G., Bac N., Yilmaz L., J. Membrane Sci., 91 (1994), 77.10.1016/0376-7388(94)00018-2
Open DOI Search in Google Scholar Back to article
[10] Yi S.L., Su Y., Zhou J.L., Chen X.R., Su Z.G., Wan Y.H., Chinese J. Process Eng., 9 (2009), 381 (in Chinese).
Search in Google Scholar Back to article
[11] Hu C.C., Liu T.C., Lee K.R., Ruaan R.C., Lai J.Y., Desalination, 193 (2006), 14.10.1016/j.desal.2005.04.137
Search in Google Scholar Back to article
[12] Wu J.R., Chen L.M., Xu W.D., Chem. Prod. Technol., 16 (2009), 48 (in Chinese).
Search in Google Scholar Back to article
[13] Guo Z.X., Li Y., Yu J., Chem. J. Chinese U., 24 (2003), 1139.
Search in Google Scholar Back to article

Preparation of nanosized NaA zeolite and its surface modification by KH-550

Abstract

Paradigm

My account