The effect of ligand-to-Eu3+ charge-transfer transitions (LMCT) on the photoluminescence intensity of M2SiO4: Eu3+ (M = Ca, Zn) type phosphors

Öztürk, Esra; Karacaoglu, Erkul

doi:10.2478/msp-2018-0059

Abstract

In this study, silicate systems, M₂SiO₄ (M = Ca, Zn) were produced by solid state reaction and doped with 1 mol% Eu³⁺ rare-earth ion. Their heat treatments, which were conducted at 1200 °C and above for minimum 3 hours under an open atmosphere, were applied according to the DTA/TG results. Powder X-ray diffraction XRD analyses were performed to determine the phase properties of the phosphor systems after the sintering process. It was proved that the structures of two of the phosphor systems were well formed in except that the Zn₂SiO₄ had some ZnO secondary phases. The expected photoluminescence (PL) results were presented and the transitions of the Eu³⁺ ions were observed for both phosphors.

References

[1] Basavaraj R.B., Nagabhushana H., Prasad D.B., Sharma S.C., Prashantha S.C., Nagabhushana B.M., Optik, 19 (2015), 1745.10.1016/j.ijleo.2014.07.149
Search in Google Scholar Back to article
[2] Öztürk E., Karacaoglu E., J. Therm. Anal.Calorim., 120 (2015), 1139.
Search in Google Scholar Back to article
[3] Sunitha D.V., Nagabhushana H., Sharma S.C., Singh F., Nagabhushana B.M., Dhananjaya N., Shivakumara C., Chakradhar R.P.S., J. Lumin., 143 (2013), 409.10.1016/j.jlumin.2013.04.025
Search in Google Scholar Back to article
[4] Baran A., Barzowska J., Grinberg M., Mahlik S., Szczodrowski K., Zorenko Y., Opt. Mater., 35 (2013), 2107.10.1016/j.optmat.2013.05.030
Open DOI Search in Google Scholar Back to article
[5] Xie Q., Zhan P., Wang W., Li Z., Zhang Z., J. Alloy. Compd., 642 (2015), 131.10.1016/j.jallcom.2015.04.032
Search in Google Scholar Back to article
[6] Wu Y., Wangn Y., He D., Fu M., Chen Z., Li Y., J. Lumin., 130 (2010), 1768.10.1016/j.jlumin.2010.04.008
Search in Google Scholar Back to article
[7] Su F., Ma B., Ding K., Li G., Wang G., Chen W., Joly A.G., McCready D.E., J. Lumin., 116 (2006), 117.10.1016/j.jlumin.2005.03.010
Search in Google Scholar Back to article
[8] Hsu C.K., Thermochim. Acta, 392 – 393 (2002), 157.10.1016/S0040-6031(02)00097-7
Search in Google Scholar Back to article
[9] Farag H.K., Hanafi Z.M., Dawy M., Abd el Aziz E.M., CJPAS, 4 (2010), 1303.
Search in Google Scholar Back to article
[10] Hao Z., Zhang J., Zhang X., Luo Y., Zhang L., Zhao H., J. Lumin., 152 (2014), 40.10.1016/j.jlumin.2013.10.033
Search in Google Scholar Back to article
[11] Luo Y.Y., Jo D.S., Senthil K., Tezuka S., Kakihana M., Toda K., Masaki T., Yoon D.H., J. Solid State Chem., 189 (2012), 68.10.1016/j.jssc.2011.11.046
Search in Google Scholar Back to article
[12] Ye R., Ma R., Zhang C., Gao Y., Hua Y., Deng D., Liu P., Xu S., J. Alloy. Compd., 566 (2013), 73.10.1016/j.jallcom.2013.03.020
Search in Google Scholar Back to article
[13] Li Y.-C., Chang Y.-H., Lin Y.-F., Chang Y.-S., Lin Y.-J., J. Alloy. Compd., 439 (2007), 367.
Search in Google Scholar Back to article

The effect of ligand-to-Eu3+ charge-transfer transitions (LMCT) on the photoluminescence intensity of M2SiO4: Eu3+ (M = Ca, Zn) type phosphors

Abstract

Paradigm

My account