The Fractographic Investigation of an Aeroengine Accessory Gearbox Quill Shaft

Saraçyakupoğlu, Tamer

doi:10.2478/fas-2020-0004

Abstract

This paper analyzes the fracture of the quill shaft. An investigation of a twin-engine trainer aircraft incident has been reported. The incident occurred due to the right electric generator out and low oil pressure. The main failure based on the warnings and the subsequent incident was identified. The failure involved the fatigue fracture of the quill shaft on the J85 turbojet engine's accessory drive gearbox (ADG) and Input Drive Assembly (IDA). It was determined that the fracture had been originated by the torsional loads impacting the quill shaft that connects the ADG and IDA. The quill shaft was broken as the loads excessed the limit values designed by the manufacturer as a system protection part. Although the main failure was successfully identified, further analysis regarding the reaching to the triggering cause of the fracture was performed. Through the detailed fractographic and metallographic studies, the root-cause of the fracture was determined as the misalignment of the quill shaft between ADG as the driving unit and IDA as the driver unit.

References

[1] Pizarro, D. F., (2017). Análisis del compresor axial del motor GE-J85-13, Bachelor’s Thesis. Universidad Carlos III de Madrid, pp. 1-80.
Search in Google Scholar Back to article
[2] Soares, C., (2015). Gas Turbines: A Handbook of Air, Land and Sea Applications, Butterworth-Heinemann, Oxford, UK.10.1016/B978-0-12-410461-7.00001-8
Search in Google Scholar Back to article
[3] Wang, H., Yang, S., Han, L., Fan, H., & Jiang, Q. (2020). Failure Analysis of Crankshaft of Fracturing Pump. Engineering Failure Analysis, 109, 104378. DOI: 10.1016/j.engfailanal.2020.104378.10.1016/j.engfailanal.2020.104378
Search in Google Scholar Back to article
[4] Infante, V., Silva, J. M., Silvestre, M. A. R., & Baptista, R. (2012). Failure of a crankshaft of an aeroengine: A contribution for an accident investigation. Engineering Failure Analysis, 35, pp. 286-293. DOI: 10.1016/j.engfailanal.2013.02.002.10.1016/j.engfailanal.2013.02.002
Search in Google Scholar Back to article
[5] Shimamura, Y., Narita, K., Ishii, H., Tohgo, K., Fujii, T., Yagasaki, T., & Harada, M. (2014). Fatigue properties of carburized alloy steel in very high cycle regime under torsional loading. International Journal of Fatigue, 60, pp. 57-62. DOI: 10.1016/j.ijfatigue.2013.06.016.10.1016/j.ijfatigue.2013.06.016
Search in Google Scholar Back to article
[6] Saraçyakupoğlu, T. (2021). Failure analysis of J85-CAN-15 turbojet engine compressor disc. Engineering Failure Analysis, 119, 104975. DOI: 10.1016/j.engfailanal.2020.104975.10.1016/j.engfailanal.2020.104975
Search in Google Scholar Back to article
[7] Rolls-Royce, (2015). The Jet Engine, 5th Edition, Birmingham, UK. ISBN: 978-1-119-06599-9.
Search in Google Scholar Back to article
[8] Zeise, B., Liebich, R., & Prölß, M. (2014). Simulation of fretting wear evolution for fatigue endurance limit estimation of assemblies. Wear, 316 (1-2), pp. 49-57. DOI: 10.1016/j.wear.2014.04.01310.1016/j.wear.2014.04.013
Search in Google Scholar Back to article
[9] Zhang, J., Chen, Y., Xu, B., Pan, M., & Chao, Q. (2019). Effects of splined shaft bending rigidity on cylinder tilt behaviour for high-speed electro-hydrostatic actuator pumps. Chinese Journal of Aeronautics, 32 (2), pp. 499-512. DOI: 10.1016/j.cja.2018.03.00710.1016/j.cja.2018.03.007
Search in Google Scholar Back to article
[10] Zerbst, U., Madia, M., Klinger, C., Bettge, D., & Murakami, Y. (2019). Defects as a root cause of fatigue failure of metallic components. III: Cavities, dents, corrosion pits, scratches. Engineering Failure Analysis, 97, pp. 759-776. DOI: 10.1016/j.engfailanal.2019.01.034.10.1016/j.engfailanal.2019.01.034
Search in Google Scholar Back to article

The Fractographic Investigation of an Aeroengine Accessory Gearbox Quill Shaft

Abstract

Paradigm

My account