Bioactivity of a sol–gel-derived hydroxyapatite coating on titanium implants in vitro and in vivo Cover

Bioactivity of a sol–gel-derived hydroxyapatite coating on titanium implants in vitro and in vivo

Asian Biomedicine
Volume 12 (2018): Issue 1 (February 2018)
By: Jintamai Suwanprateeb,  Waraporn Suvannapruk,  Watchara Chokevivat,  Siripong Kiertkrittikhoon,  Nara Jaruwangsanti and  Prakit Tienboon  
Open Access
|Dec 2018

Figures & Tables

Figure 1

Comparison of cell proliferation on the surfaces between 20 uncoated and 20 coated (gray bars) titanium samples by methyl thiazolyl tetrazolium (MTT) assay (error bars, standard deviation, n = 4 per type per time point). Absorbance by the MTT formazan chromophore at 570 nm, and D indicates the time of incubation in days. *P < 0.05
Comparison of cell proliferation on the surfaces between 20 uncoated and 20 coated (gray bars) titanium samples by methyl thiazolyl tetrazolium (MTT) assay (error bars, standard deviation, n = 4 per type per time point). Absorbance by the MTT formazan chromophore at 570 nm, and D indicates the time of incubation in days. *P < 0.05

Figure 2

Comparison of cell mineralization on the surfaces of 20 uncoated and 20 coated (gray bars) titanium samples by Alizarin red S assay (error bars, standard deviation, n = 4 per type per time point). Absorbance by the Alizarin red S at 570 nm, and D indicates the time of incubation in days. *P < 0.05
Comparison of cell mineralization on the surfaces of 20 uncoated and 20 coated (gray bars) titanium samples by Alizarin red S assay (error bars, standard deviation, n = 4 per type per time point). Absorbance by the Alizarin red S at 570 nm, and D indicates the time of incubation in days. *P < 0.05

Figure 3

Scanning electron microscopy (SEM) images of osteoblast morphology on uncoated and coated titanium samples. a) uncoated 1 day; b) coated 1 day; c) uncoated 3 days; d) coated 3 days; e) uncoated 7 days; f ) coated 7 days; g) uncoated 14 days; h) coated 14 days; i) uncoated 21 days; and j) coated 21 days (magnification ×1000). Scale bars represent 60 μm
Scanning electron microscopy (SEM) images of osteoblast morphology on uncoated and coated titanium samples. a) uncoated 1 day; b) coated 1 day; c) uncoated 3 days; d) coated 3 days; e) uncoated 7 days; f ) coated 7 days; g) uncoated 14 days; h) coated 14 days; i) uncoated 21 days; and j) coated 21 days (magnification ×1000). Scale bars represent 60 μm

Figure 4

Extraction torque from bone of 12 uncoated and 12 coated titanium screws at different implantation periods (wks, weeks) (error bars, standard deviation, n = 4 per type per time point). *P < 0.05
Extraction torque from bone of 12 uncoated and 12 coated titanium screws at different implantation periods (wks, weeks) (error bars, standard deviation, n = 4 per type per time point). *P < 0.05

Figure 5

Scanning electron microscopy (SEM) image of uncoated and coated screws extracted from the bone. No detachment of the coating from the underlying screw is noted. Arrows indicate bone fragments (BFs). The amount and size of the BFs increased with increasing implantation periods. a) uncoated 7 weeks; b) coated 7 weeks; c) uncoated 12 weeks; d) coated 12 weeks; e) uncoated 24 weeks; and f ) coated 24 weeks (magnification ×100). Scale bars represent 1 mm
Scanning electron microscopy (SEM) image of uncoated and coated screws extracted from the bone. No detachment of the coating from the underlying screw is noted. Arrows indicate bone fragments (BFs). The amount and size of the BFs increased with increasing implantation periods. a) uncoated 7 weeks; b) coated 7 weeks; c) uncoated 12 weeks; d) coated 12 weeks; e) uncoated 24 weeks; and f ) coated 24 weeks (magnification ×100). Scale bars represent 1 mm

Figure 6

Histology of bone healing around the hydroxyapatite-coated and -uncoated screws in New Zealand white rabbits at 7 weeks, 12 weeks, and 24 weeks after surgery. Hematoxylin and eosin staining demonstrates bone remodeling comprising bone trabeculae with mixed woven bone and lamellar bone. Mature lamellar bone is only observed in coated sample at 24 weeks of implantation. a) uncoated 7 weeks; b) coated 7 weeks; c) uncoated 12 weeks; d) coated 12 weeks; e) uncoated 24 weeks; and f ) coated 24 weeks (magnification ×100; Ti, titanium; B, bone). Scale bars represent 200 μm
Histology of bone healing around the hydroxyapatite-coated and -uncoated screws in New Zealand white rabbits at 7 weeks, 12 weeks, and 24 weeks after surgery. Hematoxylin and eosin staining demonstrates bone remodeling comprising bone trabeculae with mixed woven bone and lamellar bone. Mature lamellar bone is only observed in coated sample at 24 weeks of implantation. a) uncoated 7 weeks; b) coated 7 weeks; c) uncoated 12 weeks; d) coated 12 weeks; e) uncoated 24 weeks; and f ) coated 24 weeks (magnification ×100; Ti, titanium; B, bone). Scale bars represent 200 μm
DOI: https://doi.org/10.1515/abm-2018-0029 | Journal eISSN: 1875-855X | Journal ISSN: 1905-7415
Journal RSS Feed
Language: English
Page range: 35 - 44
Published on: Dec 31, 2018
Published by: Chulalongkorn University
In partnership with: Paradigm Publishing Services
Publication frequency: 6 issues per year
Keywords:
bone–implant interface,
bone remodeling,
hydroxyapatites,
osseointegration,
sol–gel process
Related subjects:
Medicine,
Assistive professions, nursing,
Basic medical science,
Basic medical science, other,
Clinical medicine,
Clinical medicine, other

© 2018 Jintamai Suwanprateeb, Waraporn Suvannapruk, Watchara Chokevivat, Siripong Kiertkrittikhoon, Nara Jaruwangsanti, Prakit Tienboon, published by Chulalongkorn University
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Previous articleVolume 12 (2018): Issue 1 (February 2018)Next article