Synthesis of maghemite (γ-Fe2O3) nanoparticles by thermal-decomposition of magnetite (Fe3O4) nanoparticles

In this research work, we prepared γ-Fe2O3 nanoparticles by thermal-decomposition of Fe3O4. The Fe3O4 nanoparticles were synthesized via co-precipitation method at room temperature. This simple, soft and cheap method is suitable for preparation of iron oxide nanoparticles (γ-Fe2O3; Fe3O4). The samples were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), vibrating sample magnetometer and differential scanning calorimeter (DSC). The XRD and FT-IR results indicated the formation of γ-Fe2O3 and Fe3O4 nanoparticles. The TEM images showed that the γ-Fe2O3 and Fe3O4 were spherical, and their size was 18 and 22 nm respectively. Magnetic properties have been measured by VSM at room temperature. Hysteresis loops showed that the γ-Fe2O3 and Fe3O4 nanoparticles were super-paramagnetic.