Abstract
The special attention has been paid to the influence of misorientation angle of a random grain boundary (GB) on susceptibility to intergranular attack. The detailed observations of the microstructure of the intergranular corrosion (IGC) in 2024-T3 aluminium alloy (AA2024-T3) subjected to galvanic corrosion tests in two different solutions containing chloride ions (0.1 M and 0.5 M NaCl) were carried out using Scanning Electron Microscopy (SEM). The Electron Backscattered Diffraction (EBSD) technique was used to determine the grain boundary character distribution (GBCD) in the initial sample and a GBCD of corroded grain boundaries on a sample subjected to the corrosion test. The results are discussed in terms of the influence of the misorientation angle on the susceptibility of the grain boundaries to corrosion.