Preparation of ternary (35 – x)Sb2O3–xBi2O3–65P2O5 glasses for lead-free glass application

Li, Yu-Ting; Zhang, Jing-Jing; Wang, Zhi-Qiang; Xu, Fei-Long; Lin, Hai

doi:10.2478/msp-2019-0088

Abstract

Glasses composed of ternary components (35 – x)Sb₂O₃–xBi₂O₃–65P₂O₅ (0 ⩽ x ⩽ 20 mol%) have been prepared and investigated as a potential alternative to lead-free glass for low temperature applications. Their structural properties were studied by Infrared Spectroscopy IR and Differential Thermal Analysis DTA. Results from the IR showed that Sb³⁺ and Bi³⁺ were responsible for glass network structure, which was supported by the diversification of density ρ and molar volume V_m with an increasing amount of Bi₂O₃. Glass transition temperature T_g, thermal stability, and coefficient of thermal expansion increased after substitution of Bi₂O₃ for Sb₂O₃ within the range of 0 mol% to 20 mol%. The water durability decreased and then increased; it could be attributed to the corrosion resistant P–O–Sb bonds. A typical sample of 25Sb₂O₃–10Bi₂O₃–65P₂O₅ possesses excellent properties and can be a promising candidate for further applications.

References

[1] Gu S.Y., Wang Z.Q., Jiang S.W., Lin H., Ceram. Int., 40 (2014), 7643.
Search in Google Scholar Back to article
[2] Huang B., Gan W.P., Guo G.G., Li Y, Liu X., Ceram. Int., 40 (2014), 393.10.1016/j.ceramint.2013.06.014
Search in Google Scholar Back to article
[3] Bobkov A.N.M., J. Glass. Phys. Chem. Glasses, 38 (2012), 180.10.1134/S108765961201004X
Search in Google Scholar Back to article
[4] Massera J., Bourhis K., Petit L., Couzi M., Hupa L., Hupa M., Videau J. J., Cardinal T.J., J. Phys. Chem. Solids, 74 (2013), 121.10.1016/j.jpcs.2012.08.010
Search in Google Scholar Back to article
[5] Li H. Y., Zhu Z.L., Yang F.L., J. Int. J. Min. Met. Mater., 19 (2012), 628.
Search in Google Scholar Back to article
[6] Kim H.J., Je S.Y., Ju Y.W., Baek J.H., Jeong J.K., Phys. Status Solidi R, 8 (2014), 924.10.1002/pssr.201409402
Search in Google Scholar Back to article
[7] Ciceo R.L., Trandafir D.L., Radu T., Ponta O., Simon V., Ceram. Int., 40 (2014), 9517.10.1016/j.ceramint.2014.02.025
Search in Google Scholar Back to article
[8] Tiwari A.N., Subbarao E.C., J. Am. Ceram. Soc., 53 (1970), 258.10.1111/j.1151-2916.1970.tb12088.x
Search in Google Scholar Back to article
[9] Zhang B., Chen Q., Song L., Li H, Hou F., J. Am. Ceram. Soc., 91 (2008), 2036.10.1111/j.1551-2916.2008.02339.x
Search in Google Scholar Back to article
[10] Qi Y.J., Wang Z.Q., Zhai S.R., Mater. Sci. -Poland, 32 (2014), 414.10.2478/s13536-014-0214-0
Search in Google Scholar Back to article
[11] Efimov A.M., J. Non-Cryst. Solids, 209 (1997), 213.10.1016/S0022-3093(97)00010-0
Search in Google Scholar Back to article
[12] Zhang B., Chen Q., Song L., J. Non-Cryst. Solids, 354 (2008), 1948.10.1016/j.jnoncrysol.2007.11.007
Search in Google Scholar Back to article
[13] Hafid M., Jermoumi T., Toreis N., Ghailassi T., Mater. Lett., 56 (2002), 486.10.1016/S0167-577X(02)00537-2
Search in Google Scholar Back to article
[14] Tang G., Li J., Lu A.X., J. Mater. Rev., 1 (2012), 122.
Search in Google Scholar Back to article
[15] Chahine A., Et-Tabirou M., Pascal J.L., J. Mater. Lett., 58 (2004), 2776.10.1016/j.matlet.2004.04.010
Search in Google Scholar Back to article
[16] Menaa B., Mizuno M., Takahashi M., Tokuda Y., Yoko T., J. Solid State Chem., 179 (2006), 492.10.1016/j.jssc.2005.11.001
Search in Google Scholar Back to article
[17] Golovin A.I., Pavlovski V.K., Shchavelev O.S., Glass. Ceram., 49 (1993), 513.10.1007/BF00678911
Search in Google Scholar Back to article
[18] Zhang B., Chen Q., Song L., Li H., Zhang J., J. Non-Cryst. Solids, 354 (2008), 1948.10.1016/j.jnoncrysol.2007.11.007
Search in Google Scholar Back to article
[19] Li H.Y., Zhu Z.L., Yang F.L., Zhang W.D., Vac. Sci., 3 (2012), 43.
Search in Google Scholar Back to article
[20] Wang M.Q., Xiong G.H., Zhang R.C., J. China Ceram. Soc., 20 (1992), 457.
Search in Google Scholar Back to article

Preparation of ternary (35 – x)Sb2O3–xBi2O3–65P2O5 glasses for lead-free glass application

Abstract

Paradigm

My account