Evaluation of the acid properties of aluminossilicate MCM-22 material synthesized under static conditions

The hydrothermal synthesis of MCM-22 zeolite was carried out using silica, sodium aluminate and hexamethyleneimine, under static conditions at 150 °C for a period of 10 days, followed by washing with deionized water, drying overnight and calcination at 650 °C. The obtained material was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM). The XRD analysis evidenced that MCM-22 presented a well defined MWW structure. The FT-IR spectrum confirmed the efficiency of the hexamethyleneimine as an organic template used to direct the structure of the MCM-22 zeolite under static conditions. The SEM image indicated that the particles are spherical in shape, with a diameter of ca. 10 μm. The acid properties of the MCM-22 zeolite, as determined by n-buthylamine adsorption, were investigated in the temperature ranges of 105 to 300 °C and 300 to 525 °C, relative to medium and strong acid sites, respectively.