Corrosion behavior of wrought magnesium alloys AZ31 and AZ61 in Hank’s solution

J. Tkacz; K. Slouková; J. Minda; J. Drábiková; S. Fintová; P. Doležal; J. Wasserbauer

doi:10.1515/kom-2016-0016

.blurhash-client-img { display: none !important; }

Corrosion behavior of wrought magnesium alloys AZ31 and AZ61 in Hank’s solution

Koroze a ochrana materiálu

Volume 60 (2016): Issue 4 (December 2016)

By: J. Tkacz, K. Slouková, J. Minda, J. Drábiková, S. Fintová, P. Doležal and J. Wasserbauer

Open Access

|Dec 2016

Abstract

Corrosion behavior of wrought magnesium alloys AZ31 and AZ61 was studied in Hank’s solution. Potentiodynamic curves measured after short-term of exposure showed higher corrosion resistance of AZ31 magnesium alloy in comparison with AZ61 magnesium alloy. On the contrary, long-term tests measured by electrochemical impedance spectroscopy showed higher corrosion resistance of AZ61 magnesium alloy in comparison with AZ31 magnesium alloy.

References

1. Jung, O.; Smeets, R.; Porchetta, D.; Kopp, A.; Ptock, Ch.; Müller, U.; Heiland, M.; Schwade, M.; Behr, B.; et al. Optimized in vitro procedure for assessing the cytocompatibility of magnesium-based biomaterials. Acta Biomaterialia 2015, 23 (1), 354-363.10.1016/j.actbio.2015.06.005
Search in Google Scholar Back to article
2. Farraro, K. F.; Kim, K. E.; Woo, S. L.; Flowers, J. R.; McCullough, M. B. Revolutionizing orthopaedic biomaterials: The potential of biodegradable and bioresorbable magnesium-based materials for functional tissue engineering. Journal of Biomechanics 2014, 47 (9), 1979-1986.10.1016/j.jbiomech.2013.12.003
Search in Google Scholar Back to article
3. Mhaede, M.; Pastorek, F.; Hadzima, B. Infl uence of shot peening on corrosion properties of biocompatible magnesium alloy AZ31 coated by dicalcium phosphate dihydrate (DCPD). Materials Science and Engineering: C 2014, 39, 330-335.
Search in Google Scholar Back to article
4. Witte, F.; Kaese, V.; Haferkamp, H.; Switzer, E.; Lindenberg, A. M.; Wirth, C. J.; Windhagen, H. In vivo corrosion of four magnesium alloys and the associated bone response. Biomaterials 2005, 26, 3557-3563.
Search in Google Scholar Back to article
5. Li, W.; Guan, S.; Chen, J.; Hu, J.; Chen, S.; Wang, L.; Zhu, S. Preparation and in vitro degradation of the composite coating with high adhesion strength on biodegradable Mg- Zn-Ca alloy, Materials Characterization 2011, 62 (12), 1158-1165.10.1016/j.matchar.2011.07.005
Search in Google Scholar Back to article
6. Homayun, B.; Afshar, A. Microstructure, mechanical properties, corrosion behavior and cytotoxicity of Mg-Zn- Al-Ca alloys as biodegradable materials. Journal of Alloys and Compounds 2014, 607, 1-10.
Search in Google Scholar Back to article
7. Bakhsheshi-Rad, H. R.; Idris, M. H.; Abdul-Kadir, M. R.; Ourdjini, A.; Medraj, M.; Daroonparvar, M.; Hamzah, E. Mechanical and bio-corrosion properties of quaternary Mg-Ca-Mn-Zn alloys compared with binary Mg-Ca alloys. Materials & Design 2014, 53, 283-292.
Search in Google Scholar Back to article
8. Song, G. Control of biodegradation of biocompatable magnesium alloys. Corrosion Science 2007, 49 (4), 1696-1701.10.1016/j.corsci.2007.01.001
Search in Google Scholar Back to article
9. Plum, L. M.; Rink, L.; Haase, H. The Essential Toxin: Impact of Zinc on Human Health. International Journal of Environmental Research and Public Health 2010, 7 (4), 1342-1365.10.3390/ijerph7041342
Search in Google Scholar Back to article
10. Salleh, E. M.; Zuhailawati, H.; Ramakrishnan, S.; Gepreel, M. A. H. A statistical prediction of density and hardness of biodegradable mechanically alloyed Mg-Zn alloy using fractional factorial design. Journal of Alloys and Compounds 2015, 644, 476-484.
Search in Google Scholar Back to article
11. Li, Q.; Jiang, G.; Wang, C.; Dong, J.; He, G. Mechanical degradation of porous titanium with entangled structure filled with biodegradable magnesium in Hanks‘ solution. Materials Science and Engineering: C 2015, 57, 349-354.
Search in Google Scholar Back to article
12. Brar, H. S.; Wong, J.; Manuel, M. V. Investigation of the mechanical and degradation properties of Mg-Sr and Mg-Zn-Sr alloys for use as potential biodegradable implant materials. Journal of the Mechanical Behavior of Biomedical Materials 2012, 7, 87-95.
Search in Google Scholar Back to article
13. Berglund, I. S.; Brar, H. S.; Dolgova, N.; Acharya, A. P.; Keselowsky, B. G.; Sarntinoranont, M.; Manuel, M. V. Synthesis and characterization of Mg-Ca-Sr alloys for biodegradable orthopedic implant applications. Journal of Biomedical Materials Research Part B: Applied Biomaterials 2012, 100B (6), 1524-1534.10.1002/jbm.b.32721
Search in Google Scholar Back to article
14. Zhang, F.; Ma, A.; Song, D.; Jiang, J.; Lu, F.; Zhang, L.; Yang, D.; Chen, J.; Improving in-vitro biocorrosion resistance of Mg-Zn-Mn-Ca alloy in Hank‘s solution through addition of cerium. Journal of Rare Earths 2015, 33 (1), 93-101.10.1016/S1002-0721(14)60388-4
Search in Google Scholar Back to article
15. Johnston, S.; Shi, Z.; Atrens, A. The infl uence of pH on the corrosion rate of high-purity Mg, AZ91 and ZE41 in bicarbonate buffered Hanks‘ solution. Corrosion Science 2015, 101, 182-192.
Search in Google Scholar Back to article
16. Abidin, N. I. Z.; Rolfe, B.; Owen, H.; Malisano, J.; Martin, D.; Hofstetter, J.; Uggowitzer, P. J.; Atrens, A. The in vivo and in vitro corrosion of high-purity magnesium and magnesium alloys WZ21 and AZ91. Corrosion Science 2013, 75, 354-366.
Search in Google Scholar Back to article
17. Han, G.; Lee, J. Y.; Kim, Y. Ch.; Park, J. H.; Kim, D. I.; Han, H. S.; Yang, S. J.; Seok, H. K. Preferred crystallographic pitting corrosion of pure magnesium in Hanks’ solution. Corrosion Science 2012, 63, 316-322.
Search in Google Scholar Back to article
18. Zeng, R. Ch.; Sun, L.; Zheng, Y. F.; Ciu, H. Z.; Han, E. H. Corrosion and characterisation of dual phase Mg-Li-Ca alloy in Hank’s solution: The influence of microstructural features. Corrosion Science 2014, 79, 69-82.
Search in Google Scholar Back to article
19. Ng, W. F.; Chiu, K. Y.; Cheng, F. T. Effect of pH on the in vitro corrosion rate of magnesium degradable implant material. Materials Science and Engineering: C 2010, 30 (6), 898-903.10.1016/j.msec.2010.04.003
Search in Google Scholar Back to article
20. Bukovinová, L.; Hadzima, B. Electrochemical characteristics of magnesium alloy AZ31 in Hank’s solution. Corrosion Engineering, Science and Technology 2012, 47 (5), 352-357.10.1179/1743278212Y.0000000033
Search in Google Scholar Back to article
21. Vander Voort, George F. Metallography, principles and practice; Materials Park, OH: ASM International, c1999.
Search in Google Scholar Back to article
22. Liu, F.; Song, Y. W.; Shan, D. Y.; Han, E. H. Corrosion behavior of AZ31 magnesium alloy in simulated acid rain solution. Transactions of Nonferrous Metals Society of China 2010, 20 (2), s638-s642.10.1016/S1003-6326(10)60553-5
Search in Google Scholar Back to article
23. Jinfeng, D.; Guangsheng, H.; Yanchun, Z.; Bei, W. Electrochemical Performance of AZ31 Magnesium Alloy under Different Processing Conditions. Rare Metal Materials and Engineering 2014, 43 (2), 316-321.10.1016/S1875-5372(14)60066-7
Search in Google Scholar Back to article
24. Mathieu, S.; Rapin, C.; Steinmetz, J.; Steinmetz, P.: A corrosion study of the main constituent phases of AZ91 magnesium alloys. Corrosion Science 2003, 45 (12), 2741-2755.10.1016/S0010-938X(03)00109-4
Search in Google Scholar Back to article
25. Pardo, A.; Merino, M. C.; Coy, A. E.; Arrabal, R.; Viejo, F.; Matykina, E. Corrosion behaviour of magnesium/aluminium alloys in 3.5 wt.% NaCl. Corrosion Science 2008, 50 (3), 823-834.10.1016/j.corsci.2007.11.005
Search in Google Scholar Back to article
26. Song, Y.; Shan, D.; Chen, R.; Zhang, F.; Han, E. H. Biodegradable behaviors of AZ31 magnesium alloy in simulated body fluid. Materials Science and Engineering: C 2009, 29 (3), 1039-1045.10.1016/j.msec.2008.08.026
Search in Google Scholar Back to article
27. Song, G.; Atrens, A.; Dargusch, M. Infl uence of microstructure on the corrosion of diecast AZ91D. Corrosion Science 1998, 41 (2), 249-273. 10.1016/S0010-938X(98)00121-8
Search in Google Scholar Back to article

Articles in this issue

DOI: https://doi.org/10.1515/kom-2016-0016 | Journal eISSN: 1804-1213 | Journal ISSN: 0452-599X

Journal RSS Feed

Language: English

Page range: 101 - 106

Published on: Dec 8, 2016

Published by: Association of Czech and Slovak Corrosion Engineers

In partnership with: Paradigm Publishing Services

Publication frequency: Volume open

Related subjects:

Industrial chemistry,

Chemical engineering

© 2016 J. Tkacz, K. Slouková, J. Minda, J. Drábiková, S. Fintová, P. Doležal, J. Wasserbauer, published by Association of Czech and Slovak Corrosion Engineers
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Volume 60 (2016): Issue 4 (December 2016)